KIMYA ABS Kevlar Filament - 500 grams
The Kimya ABS Kevlar 3D filament belongs to the styrenic polymer family. Acrylonitrile Butadiene Styrene Kevlar (ABS Kevlar) is a composite filament enriched in aramid fibers. It offers properties that are superior to a standard ABS. It provides the printed parts with increased resistance to abrasion. It is used for finished parts and tools. The Kimya ABS Kevlar 3D filament has the following properties:
- Low warpage – compared to ABS-S-
- Lighter-weight printed parts – compared to ABS Carbon-
- Complies with the REACH standard
- Product Dimensions: 20.7 × 20.5 × 6 cm; 0.8 kg
FILAMENT PROPERTIES
| PROPERTIES |
TEST METHODS |
VALUES |
| Diameter |
INS-6712 |
1.75 ± 0.1 mm
2.85 ± 0.1 mm |
| Density |
ISO 1183-1 |
1.036 g/cm3 |
| Moisture rate |
INS-6711 |
< 0.5 % |
| Melt flow index (MFI) |
ISO 1133-1 (@220°C – 10 kg) |
35 g/10min |
| Glass transition temperature (Tg) |
ISO 11357-1 DSC (10°C/min - 20-220°C) |
100 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION |
XY |
| Printing Speed |
40-70 mm/s |
| Infill |
100% - rectilinear |
| Infill Angle |
45°/-45° |
| Nozzle Temperature |
250-270°C |
| Bed T° |
90-110°C |
PRINTED SPECIMENS PROPERTIES
|
PROPERTIES |
TEST METHODS |
VALUES |
| MECHANICAL PROPERTIES |
Tensile modulus |
ISO 527-2/5A/50 |
2,188 MPa |
| Tensile Strength |
ISO 527-2/5A/50 |
30 MPa |
| Tensile strain at strength |
ISO 527-2/1A/50 |
1.8 % |
| Tensile Stress at Break |
ISO 527-2/5A/50 |
27.3 MPa |
| Tensile strain at break |
ISO 527-2/5A/50 |
3.5 % |
| Flexural modulus |
ISO 178 |
1,662 MPa |
| Flexural strength* |
ISO 178 |
> 4,4 % |
| Flexural stress at conventional deflection (3,5% strain)* |
ISO 178 |
44.9 MPa |
| Charpy impact resistance |
ISO 179-1/1eA |
5.1 kJ/m² |
| Shore Hardness |
ISO 868 |
70,1D |
| Note 1 |
*According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 |
The data should be considered as indicative values - Properties can be influenced by production conditions. |