KIMYA ABS Kevlar Filament

$ 58.20

Diameter
Size
-
+
$ 58.20
Add to wishlist

KIMYA ABS Kevlar Filament - 500 grams

The Kimya ABS Kevlar 3D filament belongs to the styrenic polymer family. Acrylonitrile Butadiene Styrene Kevlar (ABS Kevlar) is a composite filament enriched in aramid fibers. It offers properties that are superior to a standard ABS. It provides the printed parts with increased resistance to abrasion. It is used for finished parts and tools. The Kimya ABS Kevlar 3D filament has the following properties:

  • Low warpage – compared to ABS-S-
  • Lighter-weight printed parts – compared to ABS Carbon-
  • Complies with the REACH standard
  • Product Dimensions: 20.7 × 20.5 × 6 cm; 0.8 kg

FILAMENT PROPERTIES

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 1.75 ± 0.1 mm
2.85 ± 0.1 mm
Density ISO 1183-1 1.036 g/cm3
Moisture rate INS-6711 < 0.5 %
Melt flow index (MFI) ISO 1133-1 (@220°C – 10 kg) 35 g/10min
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min - 20-220°C) 100 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION XY
Printing Speed 40-70 mm/s
Infill 100% - rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 250-270°C
Bed T° 90-110°C

PRINTED SPECIMENS PROPERTIES

PROPERTIES TEST METHODS VALUES
MECHANICAL PROPERTIES Tensile modulus ISO 527-2/5A/50 2,188 MPa
Tensile Strength ISO 527-2/5A/50 30 MPa
Tensile strain at strength ISO 527-2/1A/50 1.8 %
Tensile Stress at Break ISO 527-2/5A/50 27.3 MPa
Tensile strain at break ISO 527-2/5A/50 3.5 %
Flexural modulus ISO 178 1,662 MPa
Flexural strength* ISO 178 > 4,4 %
Flexural stress at conventional deflection (3,5% strain)* ISO 178 44.9 MPa
Charpy impact resistance ISO 179-1/1eA 5.1 kJ/m²
Shore Hardness ISO 868 70,1D
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.