KIMYA PEBA-S Filament - 500 grams
The Kimya PEBA-S 3D filament is a thermoplastic elastomer. Polyether block amide (PEBA) is produced via polycondensation of a carboxylic acid polyamide with an alcohol-terminated polyether. PEBA, based on PEBAX by Arkema, is very flexible: it has the best elongation % in the range (>550%). It can be used to make shoe soles or other sports equipment (cycling, golf, American football helmet) as it offers substantial energy return. The Kimya PEBA-S 3D filament has the following properties:
- Flexibility (>550% tensile elongation at break)
- Impact resistance
- Complies with the RoHS and REACH standards
- Product Dimensions: 20.7 × 20.5 × 6 cm; 0.8 kg
FILAMENT PROPERTIES
| PROPERTIES |
TEST METHODS |
VALUES |
| Diameter |
INS-6712 |
1.75 ± 0.1 mm
2.85 ± 0.1 mm |
| Density |
ISO 1183-1 |
1.013 g/cm3 |
| Moisture rate |
INS-6711 |
< 1 % |
| Melt flow index (MFI) |
ISO 1133-1 (@220°C – 10 kg) |
13.6 g/10min |
| Melting Temperature (Tm) |
ISO 11357-1 DSC (10°C/min – -90-190°C) |
149 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION |
XY |
| Printing Speed |
20-60 mm/s |
| Infill |
100% - rectilinear |
| Infill Angle |
45°/-45° |
| Nozzle Temperature |
210-260°C |
| Bed T° |
70-90°C |
PRINTED SPECIMENS PROPERTIES
|
PROPERTIES |
TEST METHODS |
VALUES |
| MECHANICAL PROPERTIES |
Tensile modulus |
ISO 37/2/500 |
63 MPa |
| Tensile Strength |
ISO 37/2/500 |
32.8 MPa |
| Tensile strain at strength |
ISO 37/2/500 |
> 550 % |
| Tensile Stress at Break |
ISO 37/2/500 |
32.3 MPa |
| Tensile strain at break |
ISO 37/2/500 |
> 550 % |
| Flexural modulus |
ISO 178 |
70 MPa |
| Flexural stress at conventional deflection (3,5% strain)* |
ISO 178 |
2.4 MPa |
| Charpy impact resistance |
ISO 179-1/1eA |
No Break |
| Shore Hardness |
ISO 868 |
93A |
| Note 1 |
*According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 |
The data should be considered as indicative values - Properties can be influenced by production conditions. |