KIMYA ABS Carbon / Carbon Fiber Filament - 500 grams
The Kimya ABS Carbon 3D filament belongs to the styrenic polymer family. Acrylonitrile-butadiene-styrene-carbon (ABS Carbon) is a mixture of ABS and carbon fibers. The carbon fibers give the filament improved rigidity compared to a standard ABS. This filament is highly valued by manufacturers of drones and by modeling aficionados. It is also used to make tools. The Kimya ABS Carbon 3D filament has the following properties:
- No shrinkage
- Better tensile modulus than ABS-S
- Less warpage than ABS-S
- Complies with the REACH standard
- Product Dimensions: 20.7 × 20.5 × 6 cm; 0.8 kg
FILAMENT PROPERTIES
| PROPERTIES |
TEST METHODS |
VALUES |
| Diameter |
INS-6712 |
1.75 ± 0.1 mm
2.85 ± 0.1 mm |
| Density |
ISO 1183-1 |
1.045 g/cm3 |
| Moisture rate |
INS-6711 |
< 1 % |
| Melt flow index (MFI) |
ISO 1133-1 (@220°C – 10 kg) |
17.4 g/10min |
| Glass transition temperature (Tg) |
ISO 11357-1 DSC (10°C/min - 20-220°C) |
100 °C |
| Melting Temperature (Tm) |
ISO 11357-1 DSC (10°C/min – 20-220°C) |
30 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION |
XY |
| Printing Speed |
50-60 mm/s |
| Infill |
100% - rectilinear |
| Infill Angle |
45°/-45° |
| Nozzle Temperature |
245-270°C |
| Bed T° |
90-95°C |
PRINTED SPECIMENS PROPERTIES
|
PROPERTIES |
TEST METHODS |
VALUES |
| MECHANICAL PROPERTIES |
Tensile modulus |
ISO 527-2/5A/50 |
2,665 MPa |
| Tensile Strength |
ISO 527-2/5A/50 |
35.7 MPa |
| Tensile Stress at Break |
ISO 527-2/5A/50 |
37.5 MPa |
| Tensile strain at break |
ISO 527 |
2 % |
| Flexural modulus |
ISO 178 |
1,809 MPa |
| Flexural stress at conventional deflection (3,5% strain)* |
ISO 178 |
51.4 MPa |
| Charpy impact resistance |
ISO 179-1/1eA |
6.2 kJ/m² |
| Shore Hardness |
ISO 868 |
72.7 |
| Note 1 |
*According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 |
The data should be considered as indicative values - Properties can be influenced by production conditions. |