Jabil - TPE SEBS 1300 85A 1KG - Natural
Jabil - TPE SEBS 1300 85A 1KG - Natural
Jabil - TPE SEBS 1300 85A 1KG - Natural
Jabil - TPE SEBS 1300 85A 1KG - Natural
Jabil - TPE SEBS 1300 85A 1KG - Natural
Jabil - TPE SEBS 1300 85A 1KG - Natural
Jabil - TPE SEBS 1300 85A 1KG - Natural
Jabil - TPE SEBS 1300 85A 1KG - Natural

Jabil - TPE SEBS 1300 85A 1KG - Natural

Price:

$ 71.49

Quantity 



Also Available In:


Consumer Financing

Affirm

Business Under $10K

Quick Spark

Enterprise $10K - $10M

Envision
 

Jabil - TPE SEBS 1300 85A - Natural

Description

TPE-SEBS 1300 85A 3D printing filament is a Shore 85A elastomer that does not require drying to process and has excellent bed adhesion and ease of printing. TPE-SEBS 1300 85A has low moisture absorption and has better elasticity for applications that require high flexibility and durability. It works on all open-platform direct drive 3D printers and can be run on desktop 3D Printers with PTFE Bowden Tubes. TPE-SEBS can stretch over 500% and is much easier to print than TPU filaments.

TTPE-SEBS 85A can be used for parts that need elastomeric properties that can bend, flex and stretch without the need for a heated print bed and has demonstrated a very high success rate in printing complex geometries. TPE-SEBS is similar to rubber and other thermoplastic elastomers in its properties, soft to the touch while still being strong and flexible. It is well suited to printing parts that need to dampen vibrations or products that need to retain flexible properties under weather or heat exposure while still maintaining good elastic properties; such as seals, gaskets, no skid / no mark feet, soft touch grips for power tools, and no slip mats for auto interiors.

 

Applications

  • Products that need to retain flexible properties under weather or heat exposure
  • Parts that need to dampen vibrations
  • Complex geometries
  • Casting patterns
  • Seals / Gaskets
  • No skid / no mark feet
  • No slip mats for auto interiors
  • Soft touch grip for power tools
  • Industries include
    • Automotive
    • Aerospace
    • General Manufacturing

Advantages

    • Easier to print than TPU filament
    • Shore 85A elastomer
    • High flexibility, bend and stretch (can stretch over 500%)
    • Low moisture absorption
    • Less visible layer lines
    • Does not require drying to process

Specifications

Temp Icon

Printing Temperature:

The optimal printing range is 240° – 250°C

Temp Icon

Bed Temperature:

A bed temperature of 70°C will provide the best adhesion during printing.

Speed Icon

Printing Speed:

Base printing speed of 25 mm/s
Infill speed of 25-30 mm/s
Wall speed of 25-30 mm/s
Initial layer speed of 10 mm/s

Fan Icon

Cooling:

For best results, do not use a cooling fan while printing with TPE-SEBS.

Diameter(s):

2.85mm

Color(s):

Jabil TPE SEBS 1300 95A Black
Black
Jabil TPE SEBS 1300 95A Natural
Natural
Adhesion Icon

Bed Adhesion:

Use a brim when printing on clean glass. When using a PEI sheet, use a skirt on a clean plate. There is no need for any additional adhesion methods.

Tips Icon

Other Tips:

For best results, print TPE-SEBS 85A on a direct-drive printer. If attempting to print on a Bowden-style printer, using a PTFE or fluoropolymer-lined Bowden tube will increase success.

If the material starts to short feed or bind up in the extruder, turn down the feeder wheel tension. It is recommended to start with as little tension as possible.

Information Sheets

Compare Materials

Jabil Powders

View Powders
  UTS (Mpa)
Orientation
Tensile Modulus
(Mpa) Orientation
EaB (%)
Orientation
Unnotched Impact Energy
(J/m) Orientation
Notched Impact Energy
(J/m) Orientation
Melt
Temperature (°C)
Material XY Z XY Z XY z XY XY  
PA 4000 46 37 1790 1130 34 12 1010 48 182
PA 4050 GB 44 46 3390 3380 6 5 221 33 181
PK 5000 53 51 1305 1349 41 21 1241 83 197

Jabil Filament

View Filaments
  UTS (MPa)
Orientation
Tensile Modulus
(MPa) Orientation
EaB (%)
Orientation
Unnotched Impact Energy
(J/m) Orientation
Notched Impact Energy
(J/m) Orientation
Melt
Temperature (°C)
Material XY XY XY XY XY XY
ABS 1400 LW 35 2730 3 235 39 N/A
PA 0600 49 2660 5 822 69 188
PA 4035 CF 66 6000 4 557 191 180
PA 4500 56 1930 > 100 830 62 190
PA 4535 CF 88 10600 3 525 125 190
PC 1500 FR 61 2210 6 850 51 N/A
PETg 45 1655 24 N/A N/A N/A
PETg 0800 ESD 39 1895 8 416 49 N/A
PLA 3100 47 3240 6 207 31 155
TPE SEBS 1300 85A 6 19 900 N/A N/A 163
TPE SEBS 1300 95A 11 93 780 N/A N/A 165
TPU 90A 19 13 4540 N/A N/A 220