PhotoCentric Daylight Precision Cast Resin ()()() PhotoCentric Daylight Precision Cast Resin ()()()

$ 100.00

-
+
$ 100.00
Add to wishlist

 

Key benefits include a reduced ash and residue content in burnout, no expansion when heated, highly accurate printed parts with a good smooth surface finish, highly accurate metal cast parts with a good surface finish.

ONLY for use on the Liquid Crystal Precision printer range


Viscosity

(At 25ºC Brookfield spindle 3)

630 cPs

Hardness

(ASTM D2240 After Post Exposure, 1hr UV)

75 Shore D

Tensile strength

ASTM D638 (After Post Exposure, 1h UV)

19.5 MPa

Tensile strength

ASTM D638 (Before Post Exposure)

10 MPa

Tensile Modulus

ASTM D638 (After Post Exposure, 1h UV)

1380 MPa

Elongation at break

(ASTM D638 After Post Exposure)

2-3%

Storage 

10<t>50°C

Density

1.20 g/cm3

 

Key benefits include a reduced ash and residue content in burnout, no expansion when heated, highly accurate printed parts with a good smooth surface finish, highly accurate metal cast parts with a good surface finish.

ONLY for use on the Liquid Crystal Precision printer range


Viscosity

(At 25ºC Brookfield spindle 3)

630 cPs

Hardness

(ASTM D2240 After Post Exposure, 1hr UV)

75 Shore D

Tensile strength

ASTM D638 (After Post Exposure, 1h UV)

19.5 MPa

Tensile strength

ASTM D638 (Before Post Exposure)

10 MPa

Tensile Modulus

ASTM D638 (After Post Exposure, 1h UV)

1380 MPa

Elongation at break

(ASTM D638 After Post Exposure)

2-3%

Storage 

10<t>50°C

Density

1.20 g/cm3