Jabil - TPE SEBS 1300 95A 1KG - Natural
Jabil - TPE SEBS 1300 95A 1KG - Natural
Jabil - TPE SEBS 1300 95A 1KG - Natural
Jabil - TPE SEBS 1300 95A 1KG - Natural
Jabil - TPE SEBS 1300 95A 1KG - Natural
Jabil - TPE SEBS 1300 95A 1KG - Natural
Jabil - TPE SEBS 1300 95A 1KG - Natural
Jabil - TPE SEBS 1300 95A 1KG - Natural

Jabil - TPE SEBS 1300 95A 1KG - Natural

Price:

$ 71.49
Options

Quantity 



Also Available In:


Consumer Financing

Affirm

Business Under $10K

Quick Spark

Enterprise $10K - $10M

Envision
 

Jabil - TPE SEBS 1300 95A - Natural

Description

TPE-SEBS 1300 95A 3D printing filament is a Shore 95A elastomer that does not require drying to process and has excellent bed adhesion. It also enables printing ease. TPE-SEBS 1300 95A has better elasticity for applications that require flexibility and durability with the added benefit of excellent processing and no required drying. TPE-SEBS 1300 95A is slightly firmer than the 85A product to meet application requirements that call for flexibility but also need more rigidity to achieve the finished part performance. TPE-SEBS 1300 95A works on all open-platform desktop printers and can be run on Bowden Tube or direct drive configurations.

TPE-SEBS 1300 95A can be used for parts that need elastomeric properties that can bend, flex and stretch and has demonstrated a very high success rate in printing complex geometries. TPE-SEBS 1300 95A is similar to rubber and other thermoplastic elastomers in its properties. This material has a similar feel to harder grades of TPU and TPO products with less warp, more bed adhesion and fewer printing issues. TPE-SEBS 1300 95A is well suited to printing parts that require toughness and resilience as well as some flexibility and fatigue resistance. Some common applications include (but are not limited to): automotive interior trim components, packaging closures, covers and housings, drips, no slip feet for electronic and mechanical components, and gap seals. This material is nonhygroscopic and can be printed without drying.

 

Applications

  • Parts that require toughness and resilience as well as some flexibility and fatigue resistance along with elastomeric properties that can bend, flex and stretch
  • Complex geometries
  • Automotive interior trim components
  • Packaging closures, grips, gap seals
  • Covers and housings
  • No slip feet for electronic and mechanical components
  • Industries include
    • Automotive
    • Aerospace
    • General Manufacturing

Advantages

    • High print success rates
    • Very low warpage and curl
    • No need for heated print bed or drying requirements
    • Shore 95A elastomer
    • High flexibility, bend and stretch
    • Non-hygroscopic, does not absorb moisture
    • Durable with repetitive motions
    • Less visible layer lines, less warp

Specifications

Temp Icon

Printing Temperature:

The optimal printing range is 230° – 270°C

Temp Icon

Bed Temperature:

A bed temperature of 50°C to 70°C will provide the best adhesion during printing.

Speed Icon

Printing Speed:

Base printing speed of 25 mm/s
Infill speed of 15-25 mm/s
Wall speed of 15-25 mm/s
Initial layer speed of 15-25 mm/s

Diameter(s):

1.75mm and 2.85mm

Color(s):

Jabil TPE SEBS 1300 95A Black
Black
Jabil TPE SEBS 1300 95A Natural
Natural
Fan Icon

Cooling:

For best results, do not use a cooling fan while printing with TPE-SEBS.

Adhesion Icon

Bed Adhesion:

Use a brim while printing on clean glass or a PEI sheet. No glue or extra adhesion method is necessary.

Tips Icon

Other Tips:

If the material starts to short feed or bind up in the extruder, turn down the feeder wheel tension. It is recommended to start with as little tension as possible.
Using a PTFE or fluoropolymer-lined tubing will help with printing. Using this type of tube will allow the print temperature to be lower.

Information Sheets

Compare Materials

Jabil Powders

View Powders
  UTS (Mpa)
Orientation
Tensile Modulus
(Mpa) Orientation
EaB (%)
Orientation
Unnotched Impact Energy
(J/m) Orientation
Notched Impact Energy
(J/m) Orientation
Melt
Temperature (°C)
Material XY Z XY Z XY z XY XY  
PA 4000 46 37 1790 1130 34 12 1010 48 182
PA 4050 GB 44 46 3390 3380 6 5 221 33 181
PK 5000 53 51 1305 1349 41 21 1241 83 197

Jabil Filament

View Filaments
  UTS (MPa)
Orientation
Tensile Modulus
(MPa) Orientation
EaB (%)
Orientation
Unnotched Impact Energy
(J/m) Orientation
Notched Impact Energy
(J/m) Orientation
Melt
Temperature (°C)
Material XY XY XY XY XY XY
ABS 1400 LW 35 2730 3 235 39 N/A
PA 0600 49 2660 5 822 69 188
PA 4035 CF 66 6000 4 557 191 180
PA 4500 56 1930 > 100 830 62 190
PA 4535 CF 88 10600 3 525 125 190
PC 1500 FR 61 2210 6 850 51 N/A
PETg 45 1655 24 N/A N/A N/A
PETg 0800 ESD 39 1895 8 416 49 N/A
PLA 3100 47 3240 6 207 31 155
TPE SEBS 1300 85A 6 19 900 N/A N/A 163
TPE SEBS 1300 95A 11 93 780 N/A N/A 165
TPU 90A 19 13 4540 N/A N/A 220