Jabil - PA 4035 CF - Black
Description
PA 4035 CF is a carbon fiber PA12 copolymer which provides greater stiffness, strength and toughness over similar products on the market. The high carbon fiber loading provides superior tensile strength and modulus while the PA12 base promotes relatively high ductility and ease of handling. Special formulation and processing reduce filament breakage during loading and printing. PA 4035 CF prints on any open-source desktop filament 3D printer.
PA 4035 CF is well suited for printing ducting in automotive and aerospace applications, casting patterns, composite tooling and prosthetics. For demanding applications within the aerospace and automotive industries, the filament provides high heat deflection temperatures. The dimensional stability also increases compared to standard nylon due to the additional of carbon fiber. In addition, PA 4035 CF increases stiffness and strength in load bearing orientations while showing less warping than standard nylon.
Applications
- Ducting for automotive and aerospace
- Casting patterns
- Composite tooling
- Prosthetics
- Aluminum Replacement
- Industries include:
- Medical
- Automotive
- Aerospace
- General Manufacturing
Advantages
- High strength, stiffness and toughness
- High-impact strength
- Superior printed part surface finish quality
- Surface resistivity of ≤E9 for ESD sensitive applications
- Mechanical properties can be tailored by adjusting fill orientation
- Relatively low print temperature enables use on more machines
Specifications
Printing Temperature:
The print temp range is 240 – 260°C
Bed Temperature:
The ideal bed temp is 70°C
Printing Speed:
Default Print Speed: 45 mm/s
Infill Speed: 45 mm/s
Wall Speed: 30 mm/s
Top/Bottom Speed: 25mm/s
Initial Layer Speed: 20 mm/s
Diameter(s):
1.75mm and 2.85mm
Color(s):
Cooling:
A fan speed of 100% works best.
Bed Adhesion:
Use a skirt with a thick layer of PVA glue stick on glass.
Other Tips:
Make sure to use plenty of glue on glass. If any warping occurs, use more glue.
Works well with support material. PVA support works better than HIPS.
Information Sheets
Print Settings
jabil_pa-4035-cf_print-settings.pdfTechnical Data Sheets
jabil_pa-4035-cf_technical-data-sheets.pdfSafety Data Sheets
jabil_pa-4035-cf_safety-data-sheets.pdfCompare Materials
Jabil Powders
| View Powders | |||||||||
|---|---|---|---|---|---|---|---|---|---|
| UTS (Mpa) Orientation |
Tensile Modulus (Mpa) Orientation |
EaB (%) Orientation |
Unnotched Impact Energy (J/m) Orientation |
Notched Impact Energy (J/m) Orientation |
Melt Temperature (°C) |
||||
| Material | XY | Z | XY | Z | XY | z | XY | XY | |
| PA 4000 | 46 | 37 | 1790 | 1130 | 34 | 12 | 1010 | 48 | 182 |
| PA 4050 GB | 44 | 46 | 3390 | 3380 | 6 | 5 | 221 | 33 | 181 |
| PK 5000 | 53 | 51 | 1305 | 1349 | 41 | 21 | 1241 | 83 | 197 |
Jabil Filament
| View Filaments | ||||||
|---|---|---|---|---|---|---|
| UTS (MPa) Orientation |
Tensile Modulus (MPa) Orientation |
EaB (%) Orientation |
Unnotched Impact Energy (J/m) Orientation |
Notched Impact Energy (J/m) Orientation |
Melt Temperature (°C) |
|
| Material | XY | XY | XY | XY | XY | XY |
| ABS 1400 LW | 35 | 2730 | 3 | 235 | 39 | N/A |
| PA 0600 | 49 | 2660 | 5 | 822 | 69 | 188 |
| PA 4035 CF | 66 | 6000 | 4 | 557 | 191 | 180 |
| PA 4500 | 56 | 1930 | > 100 | 830 | 62 | 190 |
| PA 4535 CF | 88 | 10600 | 3 | 525 | 125 | 190 |
| PC 1500 FR | 61 | 2210 | 6 | 850 | 51 | N/A |
| PETg | 45 | 1655 | 24 | N/A | N/A | N/A |
| PETg 0800 ESD | 39 | 1895 | 8 | 416 | 49 | N/A |
| PLA 3100 | 47 | 3240 | 6 | 207 | 31 | 155 |
| TPE SEBS 1300 85A | 6 | 19 | 900 | N/A | N/A | 163 |
| TPE SEBS 1300 95A | 11 | 93 | 780 | N/A | N/A | 165 |
| TPU 90A | 19 | 13 | 4540 | N/A | N/A | 220 |