Jabil - TPU 90A - Natural
Description
Jabil Engineered Materials TPU 90 A is an easy processing, standard product for printing jobs requiring elastomeric properties like compression set or soft touch. This filament is ideal when low scratch and mar or soft touch feel are needed along with improved impact strength. It delivers rubber-like elasticity and is resistant to abrasions and performs well even at low temperatures.
Easy printability, excellent elastomeric properties and impact strength, abrasion resistance and soft touch properties. This product has very consistent lot to lot print properties with an ISO 9001 Certificate of Analysis with every spool.
Applications
- Can be used for parts that need to maintain flexibility and/or require a resistance to oils, greases, and other solvents
- Jigs, fixtures, and tooling
- Touch pads
- Grips
- Sealss
- Soft feet with low coefficient of friction (CoF)
- No slip feet for electronic and mechanical components
- Industries include
- Automotive
- Aerospace
- General Manufacturing
Advantages
- Easy printability, very consistent results
- Abrasion resistance
- Soft-touch properties
- Impact strength
- Elastomeric properties
- Operating temperature range of -40° C to 95° C
- Good chemical resistance to oils, greases, and other solvents
Specifications
Printing Temperature:
The optimal printing range is 220° – 230°C
Bed Temperature:
Up to 50°C
Printing Speed:
Base printing speed of 20 mm/s
Infill speed of 15 mm/s
Wall speed of 18 mm/s
Initial layer speed of 15 mm/s
Diameter(s):
2.85mm
Color(s):
Cooling:
For the best results cool to 100%
Bed Adhesion:
Use a heated build plate, brim, or PVA glue stick.
Other Tips:
Use low extruder motor tension.
Information Sheets
Print Settings
jabil_tpu-90a_print-settings.pdfTechnical Data Sheets
jabil_tpu-90a_technical-data-sheets.pdfSafety Data Sheets
jabil_tpu-90a_safety-data-sheets.pdfCompare Materials
Jabil Powders
| View Powders | |||||||||
|---|---|---|---|---|---|---|---|---|---|
| UTS (Mpa) Orientation |
Tensile Modulus (Mpa) Orientation |
EaB (%) Orientation |
Unnotched Impact Energy (J/m) Orientation |
Notched Impact Energy (J/m) Orientation |
Melt Temperature (°C) |
||||
| Material | XY | Z | XY | Z | XY | z | XY | XY | |
| PA 4000 | 46 | 37 | 1790 | 1130 | 34 | 12 | 1010 | 48 | 182 |
| PA 4050 GB | 44 | 46 | 3390 | 3380 | 6 | 5 | 221 | 33 | 181 |
| PK 5000 | 53 | 51 | 1305 | 1349 | 41 | 21 | 1241 | 83 | 197 |
Jabil Filament
| View Filaments | ||||||
|---|---|---|---|---|---|---|
| UTS (MPa) Orientation |
Tensile Modulus (MPa) Orientation |
EaB (%) Orientation |
Unnotched Impact Energy (J/m) Orientation |
Notched Impact Energy (J/m) Orientation |
Melt Temperature (°C) |
|
| Material | XY | XY | XY | XY | XY | XY |
| ABS 1400 LW | 35 | 2730 | 3 | 235 | 39 | N/A |
| PA 0600 | 49 | 2660 | 5 | 822 | 69 | 188 |
| PA 4035 CF | 66 | 6000 | 4 | 557 | 191 | 180 |
| PA 4500 | 56 | 1930 | > 100 | 830 | 62 | 190 |
| PA 4535 CF | 88 | 10600 | 3 | 525 | 125 | 190 |
| PC 1500 FR | 61 | 2210 | 6 | 850 | 51 | N/A |
| PETg | 45 | 1655 | 24 | N/A | N/A | N/A |
| PETg 0800 ESD | 39 | 1895 | 8 | 416 | 49 | N/A |
| PLA 3100 | 47 | 3240 | 6 | 207 | 31 | 155 |
| TPE SEBS 1300 85A | 6 | 19 | 900 | N/A | N/A | 163 |
| TPE SEBS 1300 95A | 11 | 93 | 780 | N/A | N/A | 165 |
| TPU 90A | 19 | 13 | 4540 | N/A | N/A | 220 |