Kimya PC-FR 3D Filament - 750 grams
The Kimya PC-FR is an amorphous thermoplastic that combines the advantages of a polycarbonate with flame retardant properties linked to the formulation. This low moisture sensitive filament has good dimensional stability, a wide operating temperature range (-80 to 105°C) with its high Tg and good impact resistance . All these properties make it suitable for a variety of demanding applications such as the production of parts in the railway and automotive sectors as well as in the electrical and electronic fields. The Kimya PC-FR 3D filament has the following properties:
- Good dimensional stability
- Wide usage temperature range (-80°C à +105°C)
- Flame retardant – EN45545 class R22/R23/R24/R26 HL3, class R1/R6 HL1, HL2, HL3
- Complies with the REACH and RoHS directive
- Product Dimensions: 20.7 × 20.5 × 6 cm; 1.1 kg
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm |
| Density | ISO 1183-1 | 1.294 g/cm3 |
| Moisture rate | INS-6711 | < 0.5 % |
| Melt flow index (MFI) | ISO 1133-1 (@260°C – 2.16 kg) | 5.1 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-300°C) | 117 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 20-40 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 270-320°C |
| Bed T° | 80-115°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| THERMAL PROPERTIES | Maximum use T° | - | 105 °C |
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/5A/50 | 2,680 MPa |
| Tensile Strength | ISO 527-2/5A/50 | 66.2 MPa | |
| Tensile strain at strength | ISO 527-2/5A/50 | 3.1 % | |
| Tensile Stress at Break | ISO 527-2/5A/50 | 66.4 MPa | |
| Tensile strain at break | ISO 527-2/5A/50 | 3.1 % | |
| Flexural modulus | ISO 178 | 2,230 MPa | |
| Deformation at Flexural Strain | ISO 178 | >5 % | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 83.2 MPa | |
| Shore Hardness | ISO 868 | 80,7D |
| Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 | The data should be considered as indicative values - Properties can be influenced by production conditions. |