The Kimya PEKK-SC 3D filament belongs to the polyaryletherketone family. Polyetherketoneketone (PEKK) is a semi-crystalline thermoplastic polymer. PEKK-SC is PEKK in semi-crystalline form, imparting it with increased heat resistance. It is therefore resistant to high temperatures, abrasion and chemical products. Manufactured from KEPSTAN® Arkema, PEKK has excellent mechanical properties. Manufacturers use it to produce components exposed to acids and hydrocarbons, such as fuel and lubricants. It is compatible with the smoke/fire standard EN 45 545 – essential in the railway sector. The Kimya PEKK-SC 3D filament has the following properties:
- Semi-crystalline structure
- Excellent mechanical properties
- Heat resistance (up to 260°C)
- Railway fire and smoke standard EN45545
- Aerospace FAR 25.853 Standard
- Flame retardant – eligible to UL94 V0
- Complies with the RoHS and REACH standard
- Product Dimensions: 20.7 × 20.5 × 6 cm; 0.55 kg
FILAMENT PROPERTIES
PROPERTIES |
TEST METHODS |
VALUES |
Diameter |
INS-6712 |
1.75 ± 0.1 mm 2.85 ± 0.1 mm |
Density |
ISO 1183-1 |
1.27 g/cm3 |
Moisture rate |
INS-6711 |
< 1 % |
Melt flow index (MFI) |
ISO 1133-1 (@380°C – 5 kg) |
35 g/10min |
Glass transition temperature (Tg) |
ISO 11357-1 DSC (10°C/min - 20-410°C) |
161 °C |
Heat distortion temperature (HDT) (1.8 MPa) |
ISO 75f |
172°C |
Melting Temperature (Tm) |
ISO 11357-1 DSC (10°C/min – 20-410°C) |
332 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
PRINTING DIRECTION |
XZ |
ZX |
Infill Angle |
45°/-45° |
45°/-45° |
PRINTED SPECIMENS PROPERTIES
|
PROPERTIES |
TEST METHODS |
XZ |
ZX |
ELECTRICAL PROPERTIES |
Dielectric strength |
IEC 60243-1 (100µm) |
84 kV/mm |
84 KV/mm |
Relative permittivity |
IEC 60250 (1 MHz) |
2.6 |
2.6 |
Loss tangent |
IEC 60250 (1 kHz) |
0.007 |
0.007 |
Surface resistivity |
ASTM D257 |
1016 Ohms/m² |
1016 Ohms/m² |
Volume resistivity |
ASTM D257 |
1016 Ohms/cm |
1016 Ohms/cm |
MECHANICAL PROPERTIES |
Tensile modulus |
ISO 527-2/1A/50 |
2,448 MPa |
2,784 MPa |
Tensile Strength |
ISO 527-2/1A/50 |
64.1 MPa |
32.4 MPa |
Tensile strain at strength |
ISO 527-2/1A/50 |
4.5 % |
1.4 % |
Tensile Stress at Break |
ISO 527-2/1A/50 |
64.1 MPa |
32.4 MPa |
Tensile strain at break |
ISO 527-2/1A/50 |
4.5 % |
1.4 % |
Flexural modulus |
ISO 178 |
1,918 MPa |
1,705 MPa |
Flexural strength* |
ISO 178 |
|
62.9 % |
Flexural stress at conventional deflection (3,5% strain)* |
ISO 178 |
79.3 MPa |
61.6 MPa |
Flexural stress at break |
ISO 178 |
|
62.9 MPa |
Flexural strain at flexural strength |
ISO 178 |
|
3.8 % |
Charpy impact resistance |
ISO 179-1/1eA |
5.35 kJ/m² |
1.9 kJ/m² |
Note 1 |
*According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
Note 2 |
The data should be considered as indicative values - Properties can be influenced by production conditions. |