KIMYA PEBA-S Filament - 500 grams

The Kimya PEBA-S 3D filament is a thermoplastic elastomer. Polyether block amide (PEBA) is produced via polycondensation of a carboxylic acid polyamide with an alcohol-terminated polyether. PEBA, based on PEBAX by Arkema, is very flexible: it has the best elongation % in the range (>550%).  It can be used to make shoe soles or other sports equipment (cycling, golf, American football helmet) as it offers substantial energy return. The Kimya PEBA-S  3D filament has the following properties:

  • Flexibility (>550% tensile elongation at break)
  • Impact resistance
  • Complies with the RoHS and REACH standards
  • Product Dimensions: 20.7 × 20.5 × 6 cm; 0.8 kg

FILAMENT PROPERTIES

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 1.75 ± 0.1 mm
2.85 ± 0.1 mm
Density ISO 1183-1 1.013 g/cm3
Moisture rate INS-6711 < 1 %
Melt flow index (MFI) ISO 1133-1 (@220°C – 10 kg) 13.6 g/10min
Melting Temperature (Tm) ISO 11357-1 DSC (10°C/min – -90-190°C) 149 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION XY
Printing Speed 20-60 mm/s
Infill 100% - rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 210-260°C
Bed T° 70-90°C

PRINTED SPECIMENS PROPERTIES

PROPERTIES TEST METHODS VALUES
MECHANICAL PROPERTIES Tensile modulus ISO 37/2/500 63 MPa
Tensile Strength ISO 37/2/500 32.8 MPa
Tensile strain at strength ISO 37/2/500 > 550 %
Tensile Stress at Break ISO 37/2/500 32.3 MPa
Tensile strain at break ISO 37/2/500 > 550 %
Flexural modulus ISO 178 70 MPa
Flexural stress at conventional deflection (3,5% strain)* ISO 178 2.4 MPa
Charpy impact resistance ISO 179-1/1eA No Break
Shore Hardness ISO 868 93A
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.