KIMYA TPU-92A Filament - 750 grams
The Kimya TPU-92A 3D filament belongs to the thermoplastic polyurethane (TPU) family. It offers good resistance to heat and to the external environment as well as a Shore hardness of 92A. It can be used to print flexible, resistant parts. The Kimya TPU-92A 3D filament is used in the food, electronics, automotive and consumer goods sectors. It offers the following properties:
- Flexibility
- Resistance to abrasion
- Food contact certification EU 10/2011 and FDA 21 CFR (except black color)
- Complies with the RoHS and REACH standards
- Product Dimensions: 20.7 × 20.5 × 6 cm; 1.1 kg
FILAMENT PROPERTIES
PROPERTIES | TEST METHODS | VALUES |
Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
Density | ISO 1183-1 | 1.159 g/cm3 |
Moisture rate | INS-6711 | < 1 % |
Melt flow index (MFI) | ISO 1133-1 (@210°C – 2,16 kg) | 16.5 g/10min |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
PRINTING DIRECTION | XY |
Printing Speed | 20-70 mm/s |
Infill | 100% - rectilinear |
Infill Angle | 45°/-45° |
Nozzle Temperature | 210-250°C |
Bed T° | 60-90°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
MECHANICAL PROPERTIES | Tensile modulus | ISO 37/2/500 | 90 MPa |
Tensile Strength | ISO 37/2/500 | 43.1 MPa |
Tensile strain at strength | ISO 37/2/500 | 350 % |
Tensile Stress at Break | ISO 37/2/500 | 41.7 MPa |
Tensile strain at break | ISO 37/2/500 | 351.6 % |
Flexural modulus | ISO 178 | 81 MPa |
Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 3 MPa |
Charpy impact resistance | ISO 179-1/1eA | No Break |
Shore Hardness | ISO 868 | 92A |
Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
Note 2 | The data should be considered as indicative values - Properties can be influenced by production conditions. |