KIMYA - PEKK-A Filament - Amber

Regular price
$ 154.00
Sale price
$ 154.00
Regular price
$ 0
Sold out
Unit price
Quantity must be 1 or more

KIMYA PEKK-A Filament - 250 grams, 500 grams, 1kg

The Kimya PEKK-A 3D filament belongs to the polyaryletherketone family. Polyetherketoneketone (PEKK) is a thermoplastic polymer. PEKK-A is the amorphous form of PEKK, providing ease of printing. This is a material that boasts good mechanical properties and is resistant to high temperatures (<150°C). Produced using KEPSTAN® Arkema, the Kimya PEKK-A 3D filament has been designed for technical applications. It can come into contact with hydrocarbons and fluids, enabling it to be used in multiple business sectors: aerospace, automotive, railways, etc. It has the following properties:

  • Temperature resistance
  • Flame retardant – eligible to UL94 V0
  • Complies with the RoHS and REACH standard
  • Product Dimensions: 20.7 × 20.5 × 6 cm; 0.6 kg

FILAMENT PROPERTIES

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 1.75 ± 0.1 mm
2.85 ± 0.1 mm
Density ISO 1183-1 1.261 g/cm3
Moisture rate INS-6711 < 1 %
Melt flow index (MFI) ISO 1133-1 (@380°C – 5 kg) 37 - 47 g/10min
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min - 20-410°C) 159 °C
Heat distortion temperature (HDT) (1.8 MPa) ISO 75f 172°C
Melting Temperature (Tm) ISO 11357-1 DSC (10°C/min – 20-410°C) 308 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION XY
Printing Speed 20-40 mm/s
Infill 100% - rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 350-400°C
Bed T° 110-170°C

PRINTED SPECIMENS PROPERTIES

PROPERTIES TEST METHODS VALUES
THERMAL PROPERTIES Maximum use T° - 150 °C
Thermal conductivity ASTM E1530-11 0.21 W/mK
ELECTRICAL PROPERTIES Dielectric strength IEC 60243-1 (100µm) 84 KV/mm
Surface resistivity ASTM D257 1016 Ohms/m²
OUTGASSING Total Mass Loss (TML) ASTM E 595 0.27 %
Collected Volatile Condensable Material (CVCM) ASTM E 595 < 0.01 %
Water Vapor Recovered (WVR) ASTM E 595 0.29 %
MECHANICAL PROPERTIES Tensile modulus ISO 527-2/5A/50 2,510 MPa
Tensile Strength ISO 527-2/5A/50 65 MPa
Tensile strain at strength ISO 527-2/1A/50 5 %
Tensile Stress at Break ISO 527-2/5A/50 48 MPa
Tensile strain at break ISO 527-2/5A/50 >5 %
Flexural modulus ISO 178 1,660 MPa
Flexural stress at conventional deflection (3,5% strain)* ISO 178 63.2 MPa
Charpy impact resistance ISO 179-1/1eA 2.5 kJ/m²
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.