KIMYA ASA-S Filament - 500 grams
The 3D filament Kimya ASA-S belongs to the styrenic polymer family. Acrylonitrile styrene acrylate (ASA) is an opaque thermoplastic terpolymer. ASA offers properties close to ABS but is suitable for long-term external use. Its resistance to climatic conditions provides it with durability over time. ASA is notably used in the automotive industry.
- High weather resistance
- High UV resistance
- Complies with the RoHS and REACH standards
- Product Dimensions: 20.7 × 20.5 × 6 cm; 0.8 kg
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm |
| Density | ISO 1183-1 | 1.056 g/cm3 |
| Moisture rate | INS-6711 | < 1 % |
| Melt flow index (MFI) | ISO 1133-1 (@220°C – 10 kg) | 4 - 10 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-300°C) | 108 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 20-60 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 240-260°C |
| Bed T° | 90-100°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/5A/50 | 1,685 MPa |
| Tensile Strength | ISO 527-2/5A/50 | 38 MPa | |
| Tensile strain at strength | ISO 527-2/5A/50 | 2 % | |
| Tensile Stress at Break | ISO 527-2/5A/50 | 34.6 MPa | |
| Tensile strain at break | ISO 527-2/5A/50 | 4 % | |
| Flexural modulus | ISO 178 | 1,662 MPa | |
| Flexural strength* | ISO 178 | >5 % | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 57.3 MPa | |
| Charpy impact resistance | ISO 179-1/1eA | 13 kJ/m² | |
| Shore Hardness | ISO 868 | 74D |
| Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 | The data should be considered as indicative values - Properties can be influenced by production conditions. |