Jabil - PA 4535 CF .75KG - Black

Regular price
$ 89.99
Sale price
$ 89.99
Regular price
$ 0
Sold out
Unit price
Quantity must be 1 or more

Jabil - PA 4535 CF - Black

Description

PA 4535 CF is among the strongest PA co-polymer carbon fiber filaments available on the market, delivering increased strength and stiffness. PA 4535 CF has the highest carbon fiber loading available in the industry, providing 40% improvement in tensile strength, impact strength, Z strength and elongation at break, with the added benefit of being ESD safe.

Additionally, the combination of carbon fiber in the already extremely low-warp nylon results in extraordinarily flat prints. Typical applications for PA 4535 CF are aluminum replacement parts, housings that require tight printing dimensional tolerances, clips, brackets, retainers, covers, in addition to jigs, fixtures, and tooling.

Applications

  • Great for parts requiring increased stiffness and strength
  • Aluminum replacement parts
  • Housings requiring tight printing dimensional tolerances
  • Jigs, fixtures and tooling
  • Clips, brackets, retainers
  • Covers, housings
  • Industries include:
    • Automotive
    • Aerospace
    • General Manufacturing

Advantages

    • 40% increase in stiffness and tensile strength over lower carbon fiber-loaded products
    • No reduced impact strength
    • Improved Z layer properties
    • Electrostatic dissipative (ESD)
    • Almost no shrinkage or curl

Specifications

Printing Temperature:

The optimal printing range is 250° – 270°C

Bed Temperature:

A bed temperature of 60°C will provide the best adhesion during printing.

Printing Speed:

Base printing speed of 60 mm/s
Infill speed of 60 mm/s
Wall speed of 40 mm/s
Initial layer speed of 20 mm/s

Diameter(s):

1.75mm and 2.85mm

Color(s):

Cooling:

Fan Speed: 10%

Bed Adhesion:

PVA Glue Stick

Other Tips:

For added strength, Jabil recommends recrystallization starting with 165 - 170°C for 3-4 hours

Filament is very stiff and can create feeding issues, these can be mitigated if a small amount of moisture is absorbed from the atmosphere without sacrificing print quality.
Hardened steel or ruby tipped nozzles are required.

Information Sheets

Compare Materials

Jabil Powders

View Powders
UTS (Mpa)
Orientation
Tensile Modulus
(Mpa) Orientation
EaB (%)
Orientation
Unnotched Impact Energy
(J/m) Orientation
Notched Impact Energy
(J/m) Orientation
Melt
Temperature (°C)
Material XY Z XY Z XY z XY XY
PA 4000 46 37 1790 1130 34 12 1010 48 182
PA 4050 GB 44 46 3390 3380 6 5 221 33 181
PK 5000 53 51 1305 1349 41 21 1241 83 197

Jabil Filament

View Filaments
UTS (MPa)
Orientation
Tensile Modulus
(MPa) Orientation
EaB (%)
Orientation
Unnotched Impact Energy
(J/m) Orientation
Notched Impact Energy
(J/m) Orientation
Melt
Temperature (°C)
Material XY XY XY XY XY XY
ABS 1400 LW 35 2730 3 235 39 N/A
PA 0600 49 2660 5 822 69 188
PA 4035 CF 66 6000 4 557 191 180
PA 4500 56 1930 > 100 830 62 190
PA 4535 CF 88 10600 3 525 125 190
PC 1500 FR 61 2210 6 850 51 N/A
PETg 45 1655 24 N/A N/A N/A
PETg 0800 ESD 39 1895 8 416 49 N/A
PLA 3100 47 3240 6 207 31 155
TPE SEBS 1300 85A 6 19 900 N/A N/A 163
TPE SEBS 1300 95A 11 93 780 N/A N/A 165
TPU 90A 19 13 4540 N/A N/A 220