Jabil PETg 0800 ESD - Black
Description
Jabil Engineered Materials PETg 0800 ESD is an easy processing, electrostatic dissipative (ESD) product for printing parts that require protection from electrostatic discharge. This product has high strength and stiffness with a good balance of properties in XY and Z directions and the added benefit of ESD for jigs, fixtures and tooling that needs to safely handle electronic components.
PETg 0800 ESD filaments are easy processing and electrostatic dissipative (ESD) with a good balance of properties in XY and XYZ directions. This filament provides excellent toughness and durability.
Applications
- Jigs, fixtures, and tooling
- Housings
- End-of-arm tooling for robotics
- Brackets
- Industries include:
- Automotive
- Aerospace
- General Manufacturing
Advantages
- ESD properties - ESD of 10E5-10E9
- Good stiffness and strength
- Excellent chemical resistance
- Very consistent outer diameter and ovality of the filament
- Easy printability
- Low shrinkage and warpage
- Good continuous use temperature
Specifications
Printing Temperature:
The optimal printing range is 260° – 280°C
Bed Temperature:
A bed temperature of 80°C to 85°C will keep the prints firmly attached
Printing Speed:
Base printing speed of 60 mm/s
Infill speed of 45 mm/s
Wall speed of 40 mm/s
Initial layer speed of 30 mm/s
Cooling:
For the best mechanical properties, use a regular cooling fan speed of 5%. Increase the fan speed if better feature detail is required, up to 100%
Diameter(s):
1.75mm and 2.85mm
Color(s):
Bed Adhesion:
Firm adhesion can be obtained with PVA-based glue stick on a glass bed or PEI sheet. A brim should be used.
Other Tips:
Start with an initial layer height of at least 0.26 mm. If there is stringing, try moving the initial layer height up by increments of 0.02 mm until there is no stringing or until best print quality.
Print and store in a low humidity environment. If you experience unusual oozing, stringing or rough surface texture, the filament has likely absorbed moisture and needs to be dried.
To increase the conductivity of the printed part surface, increase the print temperature. Lowering the print temperature will reduce the conductivity of the part surface.
Information Sheets
Print Settings
jabil_petg-0800-esd_print-settings.pdfTechnical Data Sheets
jabil_petg-0800-esd_technical-data-sheets.pdfSafety Data Sheets
jabil_petg-0800-esd_safety-data-sheets.pdfCompare Materials
Jabil Powders
View Powders | |||||||||
---|---|---|---|---|---|---|---|---|---|
UTS (Mpa) Orientation |
Tensile Modulus (Mpa) Orientation |
EaB (%) Orientation |
Unnotched Impact Energy (J/m) Orientation |
Notched Impact Energy (J/m) Orientation |
Melt Temperature (°C) |
||||
Material | XY | Z | XY | Z | XY | z | XY | XY | |
PA 4000 | 46 | 37 | 1790 | 1130 | 34 | 12 | 1010 | 48 | 182 |
PA 4050 GB | 44 | 46 | 3390 | 3380 | 6 | 5 | 221 | 33 | 181 |
PK 5000 | 53 | 51 | 1305 | 1349 | 41 | 21 | 1241 | 83 | 197 |
Jabil Filament
View Filaments | ||||||
---|---|---|---|---|---|---|
UTS (MPa) Orientation |
Tensile Modulus (MPa) Orientation |
EaB (%) Orientation |
Unnotched Impact Energy (J/m) Orientation |
Notched Impact Energy (J/m) Orientation |
Melt Temperature (°C) |
|
Material | XY | XY | XY | XY | XY | XY |
ABS 1400 LW | 35 | 2730 | 3 | 235 | 39 | N/A |
PA 0600 | 49 | 2660 | 5 | 822 | 69 | 188 |
PA 4035 CF | 66 | 6000 | 4 | 557 | 191 | 180 |
PA 4500 | 56 | 1930 | > 100 | 830 | 62 | 190 |
PA 4535 CF | 88 | 10600 | 3 | 525 | 125 | 190 |
PC 1500 FR | 61 | 2210 | 6 | 850 | 51 | N/A |
PETg | 45 | 1655 | 24 | N/A | N/A | N/A |
PETg 0800 ESD | 39 | 1895 | 8 | 416 | 49 | N/A |
PLA 3100 | 47 | 3240 | 6 | 207 | 31 | 155 |
TPE SEBS 1300 85A | 6 | 19 | 900 | N/A | N/A | 163 |
TPE SEBS 1300 95A | 11 | 93 | 780 | N/A | N/A | 165 |
TPU 90A | 19 | 13 | 4540 | N/A | N/A | 220 |