Jabil - PC 1500 FR - Black
Description
Jabil’s PC 1500 FR is a flame-retardant, easy printing polycarbonate manufactured with FR UL V-0 material for durable parts. The material is perfect for parts that require strength, stiffness and impact resistance with flame retardancy. The PC 1500 FR testing performed in a qualified lab demonstrates V-0 burn properties on a printed part down to 1mm thickness when printed with the correct design and print parameters as outlined below.
Polycarbonate is an engineering material that can be challenging to print. A slurry of ABS in acetone or a PVP-based glue stick will provide strong bed adhesion during printing with clean release upon cooling. Made from UL V-0 Yellow Card certified raw materials, Jabil’s PC 1500 FR can be printed on Direct Drive and Bowden Tube 3D printers. This material, with its flame-retardant properties, is used in the aerospace and automotive industries.
Applications
- Welding fixtures
- Housings
- Motor mounts
- Aerospace parts
- Industries include:
- Automotive
- Aerospace
- General Manufacturing
Advantages
- Made from UL V-0 yellow-card-certified raw materials
- Stiff with excellent impact strength and ductility
- Very good flame retardancy and self-extinguishing properties
- High impact resistance
- Testing performed in a qualified lab demonstrates V-0 burn properties on a printed part down to 2mm thickness (*when printed with the correct design and print parameters)
Specifications
Printing Temperature:
The optimal printing range is 285° – 305°C
Bed Temperature:
Up to 105°C with ABS slurry, or up to 140°C using a PVP-based glue stick.
Printing Speed:
Base printing speed of 40 mm/s
Infill speed of 40 mm/s
Wall speed of 32 mm/s
Initial layer speed of 20 mm/s
Diameter(s):
1.75mm and 2.85mm
Color(s):
Cooling:
For best results, do not use a cooling fan. Enabling bridging settings will help improve overhang quality.
Bed Adhesion:
Suitable adhesion can be obtained by using a slurry of ABS in acetone, or with a PEI sheet with a PVP-based glue stick. A brim should be used to help with bed adhesion.
Other Tips:
If possible, print in an enclosed area that can maintain a temperature of 50-55°C to help minimize warping or cracking.
Information Sheets
Print Settings
jabil_pc-1500-fr_print-settings.pdfTechnical Data Sheets
jabil_pc-1500-fr_technical-data-sheets.pdfSafety Data Sheets
jabil_pc-1500-fr_safety-data-sheets.pdfCompare Materials
Jabil Powders
| View Powders | |||||||||
|---|---|---|---|---|---|---|---|---|---|
| UTS (Mpa) Orientation |
Tensile Modulus (Mpa) Orientation |
EaB (%) Orientation |
Unnotched Impact Energy (J/m) Orientation |
Notched Impact Energy (J/m) Orientation |
Melt Temperature (°C) |
||||
| Material | XY | Z | XY | Z | XY | z | XY | XY | |
| PA 4000 | 46 | 37 | 1790 | 1130 | 34 | 12 | 1010 | 48 | 182 |
| PA 4050 GB | 44 | 46 | 3390 | 3380 | 6 | 5 | 221 | 33 | 181 |
| PK 5000 | 53 | 51 | 1305 | 1349 | 41 | 21 | 1241 | 83 | 197 |
Jabil Filament
| View Filaments | ||||||
|---|---|---|---|---|---|---|
| UTS (MPa) Orientation |
Tensile Modulus (MPa) Orientation |
EaB (%) Orientation |
Unnotched Impact Energy (J/m) Orientation |
Notched Impact Energy (J/m) Orientation |
Melt Temperature (°C) |
|
| Material | XY | XY | XY | XY | XY | XY |
| ABS 1400 LW | 35 | 2730 | 3 | 235 | 39 | N/A |
| PA 0600 | 49 | 2660 | 5 | 822 | 69 | 188 |
| PA 4035 CF | 66 | 6000 | 4 | 557 | 191 | 180 |
| PA 4500 | 56 | 1930 | > 100 | 830 | 62 | 190 |
| PA 4535 CF | 88 | 10600 | 3 | 525 | 125 | 190 |
| PC 1500 FR | 61 | 2210 | 6 | 850 | 51 | N/A |
| PETg | 45 | 1655 | 24 | N/A | N/A | N/A |
| PETg 0800 ESD | 39 | 1895 | 8 | 416 | 49 | N/A |
| PLA 3100 | 47 | 3240 | 6 | 207 | 31 | 155 |
| TPE SEBS 1300 85A | 6 | 19 | 900 | N/A | N/A | 163 |
| TPE SEBS 1300 95A | 11 | 93 | 780 | N/A | N/A | 165 |
| TPU 90A | 19 | 13 | 4540 | N/A | N/A | 220 |